| Subject | Object |
|---|---|
| gptkb:HP_3D_High_Reusability_PA_12 | 48 MPa |
| gptkb:High-density_polyethylene_(HDPE) | 31 to 38 MPa |
| gptkb:UNS_N10276 | 690 MPa (min) |
| gptkb:Nylon_66 | high |
| gptkb:Ultem | 110 MPa |
| gptkb:N06625 | high |
| gptkb:Carbyne | higher than graphene (theoretical) |
| gptkb:Polythene | Varies by type |
| gptkb:Zylon | 5.8 GPa |
| gptkb:Nylon_6,6 | high |
| gptkb:Hastelloy_C-276 | 690 MPa (min) |
| gptkb:Monel_400 | 480–620 MPa |
| gptkb:low-density_polyethylene_(LDPE) | 8–12 MPa |
| gptkb:PolyMide_PA6 | 66 MPa |
| gptkb:AISI_4140 | 655–1590 MPa |
| gptkb:Nylon_6 | high |
| gptkb:UNS_N06600 | 550 MPa minimum |
| gptkb:C29000 | 275-345 MPa |
| gptkb:S235 | 360-510 MPa |
| gptkb:Nimonic_75 | ~750 MPa |