Statements (43)
| Predicate | Object |
|---|---|
| gptkbp:instanceOf |
gptkb:nickel-based_superalloy
|
| gptkbp:composedOf |
carbon
iron cobalt nickel manganese silicon molybdenum tungsten chromium lanthanum |
| gptkbp:corrosionResistance |
excellent
|
| gptkbp:density |
8.95 g/cm³
|
| gptkbp:developedBy |
gptkb:Haynes_International
|
| gptkbp:form |
gptkb:bar
gptkb:tube sheet pipe plate weld wire |
| gptkbp:introducedIn |
1980s
|
| gptkbp:maxServiceTemperature |
1150°C
|
| gptkbp:notableFor |
oxidation resistance
high temperature strength creep resistance fabricability |
| gptkbp:specifies |
gptkb:ASTM_B619
gptkb:ASTM_B622 gptkb:ASTM_B626 ASTM B435 ASTM B572 |
| gptkbp:tensileStrength |
760 MPa at room temperature
|
| gptkbp:thermalStability |
high
|
| gptkbp:UNNumber |
N06230
|
| gptkbp:usedIn |
gas turbines
aerospace applications combustion chambers furnace components industrial heating equipment |
| gptkbp:weldability |
good
|
| gptkbp:bfsParent |
gptkb:Haynes_alloys
|
| gptkbp:bfsLayer |
8
|
| https://www.w3.org/2000/01/rdf-schema#label |
Haynes 230
|