gptkbp:instanceOf
|
aluminum alloy
|
|
gptkbp:alsoKnownAs
|
Hastelloy C276
|
|
gptkbp:carbonContent
|
0.01% max
|
|
gptkbp:chromiumContent
|
14.5-16.5%
|
|
gptkbp:cobaltContent
|
2.5% max
|
|
gptkbp:containsElement
|
gptkb:phosphorus
gptkb:sulfur
carbon
iron
cobalt
nickel
manganese
silicon
molybdenum
tungsten
vanadium
chromium
|
|
gptkbp:corrosionResistance
|
excellent
|
|
gptkbp:density
|
8.89 g/cm3
|
|
gptkbp:elongation
|
40% (min)
|
|
gptkbp:formability
|
good
|
|
https://www.w3.org/2000/01/rdf-schema#label
|
UNS N10276
|
|
gptkbp:ironContent
|
4-7%
|
|
gptkbp:magnetType
|
non-magnetic
|
|
gptkbp:mainProducer
|
gptkb:Haynes_International
gptkb:Special_Metals_Corporation
|
|
gptkbp:manganeseContent
|
1% max
|
|
gptkbp:meltingPoint
|
1325-1370°C
|
|
gptkbp:molybdenumContent
|
15-17%
|
|
gptkbp:nickelContent
|
balance
|
|
gptkbp:phosphorusContent
|
0.04% max
|
|
gptkbp:resistantTo
|
chloride stress corrosion cracking
oxidizing acids
crevice corrosion
pitting
reducing acids
|
|
gptkbp:siliconContent
|
0.08% max
|
|
gptkbp:standardizedBy
|
gptkb:ASTM_B564
gptkb:ASTM_B575
gptkb:ASTM_B619
gptkb:ASTM_B622
gptkb:ASTM_B626
|
|
gptkbp:sulfurContent
|
0.03% max
|
|
gptkbp:tensileStrength
|
690 MPa (min)
|
|
gptkbp:tungstenContent
|
3-4.5%
|
|
gptkbp:UNNumber
|
N10276
|
|
gptkbp:usedIn
|
marine engineering
chemical processing
pollution control
pulp and paper industry
waste treatment
|
|
gptkbp:weldability
|
good
|
|
gptkbp:yield
|
283 MPa (min)
|
|