gptkbp:instanceOf
|
gptkb:corrosion-resistant_alloy
gptkb:nickel-molybdenum-chromium_superalloy
|
|
gptkbp:carbonContent
|
max 0.01%
|
|
gptkbp:chromiumContent
|
approx. 15.5%
|
|
gptkbp:cobaltContent
|
max 2.5%
|
|
gptkbp:containsElement
|
gptkb:phosphorus
gptkb:sulfur
carbon
iron
cobalt
nickel
manganese
silicon
molybdenum
tungsten
vanadium
chromium
|
|
gptkbp:corrosionResistance
|
excellent in reducing and oxidizing environments
|
|
gptkbp:density
|
8.89 g/cm³
|
|
gptkbp:developedBy
|
gptkb:Haynes_International
|
|
gptkbp:elongation
|
40% (min)
|
|
gptkbp:formability
|
good
|
|
gptkbp:ironContent
|
approx. 5%
|
|
gptkbp:manganeseContent
|
max 1%
|
|
gptkbp:meltingPoint
|
1325–1370°C
|
|
gptkbp:molybdenumContent
|
approx. 16%
|
|
gptkbp:nickelContent
|
approx. 57%
|
|
gptkbp:phosphorusContent
|
max 0.04%
|
|
gptkbp:resistantTo
|
crevice corrosion
pitting
stress corrosion cracking
|
|
gptkbp:siliconContent
|
max 0.08%
|
|
gptkbp:standardNumber
|
gptkb:ASTM_B366
gptkb:ASTM_B564
gptkb:ASTM_B575
gptkb:ASTM_B619
gptkb:ASTM_B622
gptkb:ASTM_B626
gptkb:UNS_N10276
|
|
gptkbp:sulfurContent
|
max 0.03%
|
|
gptkbp:tensileStrength
|
690 MPa (min)
|
|
gptkbp:trademarkOf
|
gptkb:Haynes_International
|
|
gptkbp:tungstenContent
|
approx. 4%
|
|
gptkbp:usedIn
|
gptkb:oil_and_gas_industry
marine engineering
chemical processing
pollution control
waste treatment
pharmaceutical production
pulp and paper production
|
|
gptkbp:vanadiumContent
|
max 0.35%
|
|
gptkbp:weldability
|
good
|
|
gptkbp:yield
|
283 MPa (min)
|
|
gptkbp:bfsParent
|
gptkb:Hastelloy_C
|
|
gptkbp:bfsLayer
|
7
|
|
https://www.w3.org/2000/01/rdf-schema#label
|
Hastelloy C-276
|