gptkbp:instanceOf
|
nickel-chromium alloy
|
|
gptkbp:alsoKnownAs
|
gptkb:Inconel_600
|
|
gptkbp:chromiumContent
|
14-17% nominal
|
|
gptkbp:coefficientOfExpansion
|
13.3 µm/m·K at 20–100°C
|
|
gptkbp:containsElement
|
iron
nickel
chromium
|
|
gptkbp:corrosionResistance
|
high
|
|
gptkbp:density
|
8.47 g/cm³
|
|
gptkbp:developedBy
|
gptkb:International_Nickel_Company
|
|
gptkbp:elongation
|
30% min (annealed)
|
|
gptkbp:form
|
gptkb:bar
sheet
pipe
tube
fittings
forgings
plate
|
|
gptkbp:hardness
|
85 HRB max (annealed)
|
|
gptkbp:heatTreatment
|
solution annealed
|
|
https://www.w3.org/2000/01/rdf-schema#label
|
Alloy 600
|
|
gptkbp:ironContent
|
6-10% nominal
|
|
gptkbp:magnetType
|
non-magnetic
|
|
gptkbp:meltingPoint
|
1354–1413°C
|
|
gptkbp:nickelContent
|
72% nominal
|
|
gptkbp:notableFor
|
excellent mechanical properties at high temperatures
|
|
gptkbp:oxidationResistance
|
high
|
|
gptkbp:resistantTo
|
organic acids
alkalis
chloride-ion stress corrosion cracking
oxidizing conditions
reducing conditions
|
|
gptkbp:specifies
|
gptkb:ASTM_B166
gptkb:ASTM_B167
gptkb:ASTM_B168
gptkb:ASTM_B366
gptkb:ASTM_B564
gptkb:UNS_N06600
|
|
gptkbp:tensileStrength
|
550 MPa min (annealed)
|
|
gptkbp:thermalConductivity
|
14.9 W/m·K at 100°C
|
|
gptkbp:usedIn
|
aerospace
food processing
nuclear reactors
chemical processing
heat treating equipment
gas turbine components
|
|
gptkbp:vulnerableTo
|
intergranular attack in some environments
|
|
gptkbp:weldability
|
good
|
|
gptkbp:yield
|
240 MPa min (annealed)
|
|