Statements (50)
| Predicate | Object |
|---|---|
| gptkbp:instanceOf |
nickel-based superalloy
|
| gptkbp:aluminiumContent |
about 1.5%
|
| gptkbp:chromiumContent |
about 19.5%
|
| gptkbp:cobaltContent |
about 18%
|
| gptkbp:containsElement |
gptkb:phosphorus
gptkb:sulfur carbon iron boron cobalt nickel aluminium manganese silicon titanium zirconium chromium |
| gptkbp:density |
8.18 g/cm³
|
| gptkbp:developedBy |
Henry Wiggin & Co
|
| gptkbp:form |
bars
sheets wires forgings strips |
| gptkbp:hardness |
Rockwell B 100-105
|
| gptkbp:heatTreatment |
solution treated and aged
|
| https://www.w3.org/2000/01/rdf-schema#label |
Nimonic 90
|
| gptkbp:introducedIn |
1940s
|
| gptkbp:maxOperatingTemperature |
up to 920°C
|
| gptkbp:nickelContent |
about 57%
|
| gptkbp:property |
oxidation resistance
creep resistance good corrosion resistance high-temperature strength |
| gptkbp:relatedAlloy |
gptkb:Nimonic_75
gptkb:Nimonic_80A |
| gptkbp:standardizedBy |
gptkb:ASTM_B637
BS HR2 UNS N07090 W. Nr. 2.4632 |
| gptkbp:tensileStrength |
up to 1000 MPa
|
| gptkbp:titaniumContent |
about 2.5%
|
| gptkbp:usedIn |
nuclear engineering
aerospace components turbine discs gas turbine blades hot-working tools |
| gptkbp:weldability |
good
|
| gptkbp:bfsParent |
gptkb:Nimonic
|
| gptkbp:bfsLayer |
7
|