gptkbp:instanceOf
|
stainless steel grade
|
|
gptkbp:alternativeTo
|
316 stainless steel
|
|
gptkbp:carbonContentMax
|
0.03%
|
|
gptkbp:chromiumContentRange
|
16-18%
|
|
gptkbp:containsElement
|
carbon
iron
nickel
molybdenum
chromium
|
|
gptkbp:corrosionResistance
|
superior to 304 stainless steel
|
|
gptkbp:density
|
8.0 g/cm³
|
|
gptkbp:differenceFrom316
|
lower carbon content
|
|
gptkbp:DINStandard
|
1.4404
|
|
gptkbp:formability
|
good
|
|
gptkbp:hardnessMax
|
95 HRB
|
|
gptkbp:hasFeature
|
ASTM A240
EN 1.4404
UNS S31603
|
|
gptkbp:hasProperty
|
corrosion resistance
good weldability
low carbon content
|
|
gptkbp:heatTreatment
|
not hardenable by heat treatment
|
|
https://www.w3.org/2000/01/rdf-schema#label
|
316L
|
|
gptkbp:ISOStandard
|
ISO 15510
|
|
gptkbp:JISStandard
|
SUS316L
|
|
gptkbp:magnetType
|
non-magnetic
|
|
gptkbp:mainAlloyingElement
|
chromium, nickel, molybdenum
|
|
gptkbp:meltingPoint
|
1375–1400°C
|
|
gptkbp:molybdenumContentRange
|
2-3%
|
|
gptkbp:nickelContentRange
|
10-14%
|
|
gptkbp:resistanceToCreviceCorrosion
|
high
|
|
gptkbp:resistanceToPitting
|
high
|
|
gptkbp:suitableFor
|
high chloride environments
|
|
gptkbp:surfaceFinishAvailable
|
gptkb:BA
No. 4
2B
|
|
gptkbp:susceptibilityToSensitization
|
low
|
|
gptkbp:tensileStrength
|
485 MPa (min)
|
|
gptkbp:usedFor
|
surgical instruments
orthopedic implants
architectural applications
watch cases and bands
|
|
gptkbp:usedIn
|
medical implants
food processing equipment
marine applications
pharmaceutical equipment
chemical processing equipment
|
|
gptkbp:weldability
|
excellent
|
|
gptkbp:yield
|
170 MPa (min)
|
|
gptkbp:bfsParent
|
gptkb:ASTM_A312
|
|
gptkbp:bfsLayer
|
7
|