Statements (31)
Predicate | Object |
---|---|
gptkbp:instanceOf |
gptkb:steel
|
gptkbp:carbon_content_(wt%) |
2.8
|
gptkbp:chromium_content_(wt%) |
15.25
|
gptkbp:cobalt_content_(wt%) |
2.5
|
gptkbp:containsElement |
gptkb:phosphorus
gptkb:sulfur gptkb:niobium carbon cobalt manganese silicon molybdenum vanadium chromium |
gptkbp:countryOfOrigin |
gptkb:United_States
|
gptkbp:hardness_range_(HRC) |
60-63
|
https://www.w3.org/2000/01/rdf-schema#label |
CPM S110V
|
gptkbp:manufacturer |
gptkb:Crucible_Industries
|
gptkbp:molybdenum_content_(wt%) |
2.25
|
gptkbp:niobium_content_(wt%) |
3.0
|
gptkbp:notableFor |
high corrosion resistance
high edge retention high wear resistance |
gptkbp:primaryUse |
knife blades
|
gptkbp:production_process |
gptkb:Crucible_Particle_Metallurgy_(CPM)
|
gptkbp:type |
powder metallurgy steel
|
gptkbp:used_by_knife_brands |
gptkb:Benchmade
gptkb:Spyderco |
gptkbp:vanadium_content_(wt%) |
9.0
|